1. Operation and Process
HHGS03 CO Removal Catalyst works efficiently to remove CO from petro gas, inert gas, oxygen and etc, also could be used in various furnace like oven, chimney place, incinerator to treat not burst CO.
This catalyst could make CO content less than 0.5ppm under temperature 150~200℃ and space velocity at (0.3~1.0)×104 h-1; oxygen capacity of this catalyst could be 50ml/g, and catalyze reaction CO and O2 to be CO2.
Reaction formula: CO+O2 CO Removal catalyst CO2
2. Operation Properties
Before using, CO removal catalyst should be heated up to 180~200℃ by nitrogen (fresh air is also available for high temperature exhaust gas in oven and fireplace), in order to active its performance. The optimal operating temperature is 200℃, and removal CO until 0.5ppm left under operation space velocity (0.3~1.0)×104 h-1; Max temperature is 750℃ (cooling system is required if flammable gas is in high concentration).
3. Technology Properties
No
Test item
Technology parameter
Carrier: cordierite and composite alumina with various specs
1
Space velocity
≥3×103h-1
2
Initial ignition temperature
100℃-150℃
3
Optimal service temperature
180℃-200℃
4
CO removal ratio
Service life
≥ 98﹪
≥2 years
5
≥ 2 years
6
CO outlet content
＜5ppm
7
Bulk density
0.68±0.05g/mL
8
Crushing strength
≥ 14 MPa
9
Coating component
≥ 10.0%
10
Activity component
0.1%-0.2% (also depends on your demand)
11
Expulsion ratio
＜1%
12
Appearance
Usually is light yellow (would be grey after pre-reduction)
13
Packing
Moisture-proof
14
Suggested loading height/diameter
Honeycomb type 4:1, particle 2:1